Acrylic adhesive on Glass
10 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE AA 3751 Cured @ 30 mW/cm², measured @ 365 nm, for 2 minutes using a Zeta® 7400 light source Lap Shear Strength, ISO 4587: Epoxyglass N/mm² ≥5.2LMS (psi) (≥754) Glass to Glass N/mm² *5.1 (psi) (740) | not stated | 5.1 MPa | ISO 4587 | TDS p.1 |
| LOCTITE AA 3953 Lap shear strength, ISO 4587: Glass N/mm2 5 (psi) (727). *substrate failure | not stated | 5 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA 3525 Cured @ 50 mW/cm², measured @ 365 nm, for 30 seconds using a Zeta® 7200 light source. Lap Shear Strength, ISO 4587: Glass: 0 gap N/mm2 4.7 (psi) (700) | not stated | 4.7 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: Glass 670. Cured 7 days at room temperature. | abraded | 4.6195 MPa | ASTM D1002 | TDS p.3 |
| LOCTITE AA 3951 Lap Shear Strength, ISO 4587: Glass * N/mm² 4.4 * (psi) (631) *substrate failure | not stated | 4.4 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA 3491 Lap Shear Strength, ISO 4587: Glass to Glass: 0 gap N/mm² 4.1 (psi) (600); 0.5 mm gap N/mm² 4.1 (psi) (600) | not stated | 4.1 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H8610 Glass N/mm² 3 (psi) (400) | not stated | 3 MPa | ISO 4587 | TDS p.2 |
| LOCTITE WT 3001 Glass** N/mm2 (psi) 2.5 | not stated | 2.5 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 Glass N/mm² 2 (psi) (370) | not stated | 2 MPa | ISO 4587 | TDS p.2 |
| LOCTITE WT 3003 Glass** N/mm2 (psi) 1.0 | not stated | 1 MPa | ISO 4587 | TDS p.2 |