Acrylic adhesive on Aluminum

23 °C Aluminum Etched 31 MPa (4500 lb/in²) (CF )

Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. Aluminum, etched, 23°C, 30.3 MPa (4400 lb/in²).

Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Aluminum Etched 29 MPa (4200 lb/in²) (CF ) ¹

Aluminum N/mm² 29 (psi) (4,180)

Shear Strength, psi, ASTM D1002 Typical Value Etched Aluminum 4000

Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Aluminum Light Abrasion and Solvent Clean 27 MPa (3900 lb/in²) (CF ) ¹

Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 26.9 MPa (3900 lb/in²) (CF) 23 °C Aluminum Etched

Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 26.2 MPa (3800 lb/in²) (CF) 23 °C Aluminum Etched

Primed aluminum, 4,440 3,680 ASTM D1002

Zugscher- Aluminium/Bondur F 44 (AlCuMg2pl) F 300: 18 N/mm² F 305: 25 N/mm²

Shear Strength, psi, ASTM D1002 Typical Value Aluminum 3600

Rate of Strength Buildup … Substrate: Etched Aluminum … Test Method: ASTM D1002, ISO 4587 … 7d 3,500 lb/in² ¹

Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Aluminum 24.1 MPa (3500 lb/in²) (CF) ¹

Overlap Shear Strength, dwell 24 h, ASTM D1002, ISO 4587. Aluminum, etched, 24 MPa (3465 lb/in²).

Substrate: Etched Aluminum. Dwell Time 7d Value 3,450 lb/in². Test Method: ASTM D1002, ISO 4587.

Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Aluminum 23.4 MPa (3400 lb/in²) (CF) ¹

Aluminum (etched) N/mm² 23.2 (psi) (3,360)

Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Aluminum 20.7 MPa (3000 lb/in²) (CF) ¹

Lap Shear Strength, ISO 4587: Aluminum (etched) N/mm² ≥20.6

Lap shear strength versus Thermal cycling (ISO 4587). On aluminium. Pretreatment: sandblasting. Cure: 16 hrs/40°C. 19.8 MPa. 100 cycles of 6 hours duration from -30°C to 70°C.

Lap Shear Strength, ISO 4587: Aluminum N/mm² 19 (psi) (2,800). Cured for 72 hours @ 22 °C.

Aluminum (roughened to 41 rms) N/mm² 19 (psi) (2,780)

Aluminum (abraded) N/mm2 (psi) 18 (2,610)

Lap shear strength versus thermal cycling (ISO 4587). On aluminium, cured for 16 hours at 40°C and tested at 23°C. Pretreatment - Sand blasting, isopropanol degreasing. 100 cycles of 6 hours duration from -30°C to 70°C: 17.75 MPa.

Cured for 15 minutes @ 121 °C. Lap Shear Strength, ISO 4587: Aluminum N/mm² 17.6 (psi) (2,550)

Overlap Shear Strength … Test Condition: 23 °C … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Aluminum Etched 16.6 MPa (2404 lb/in²) ¹

Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 7d Aluminum MEK/Abrade/MEK 15 MPa (2180 lb/in²) ¹

Aluminum N/mm² 15 (psi) (2,180)

Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 14.5 MPa (2101 lb/in²) 7d Aluminum MEK/Abrade/MEK

Overlap Shear Strength. Temperature: 23 °C (73 °F). Dwell Time: 7 d. Test Method: ASTM D1002, ISO 4587. Aluminum MEK/Abrade/MEK 1960 lb/in². (CF).

Anodized Aluminum 1840

Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: Aluminum (MEK/abrade/MEK) 1780. Cured 7 days at room temperature.

Tensile lap-shear strength (CQP046-6 / ISO 4587) 12 MPa A, B, C … B) Cured for 1 week at 23 °C C) Adhesive layer: 25 x 12.5 x 1.5 mm / on aluminum

Tensile lap-shear strength (CQP046-6 / ISO 4587) 12 MPa A, B, C … B) Cured for 1 week at 23 °C C) Adhesive layer: 25 x 12.5 x 1.5 mm / on aluminum

Tensile lap-shear strength (CQP046-6 / ISO 4587) 12 MPa A, B, C … B) Cured for 1 week at 23 °C C) Adhesive layer: 25 x 12.5 x 1.5 mm / on aluminum

Overlap Shear (psi); Etched Aluminum, at Temperature, ASTM D1002. DP8010NS Blue at 73°F (23°C): 1700. Cured 7 days at room temperature.

Aluminum (abraded) N/mm² 10 (psi) (1,440)

Anodized Aluminum N/mm² 10 (psi) (1,480)

Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Aluminum MEK / Abrade / MEK 6.9 MPa (995 lb/in²) ¹

Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Aluminum MEK / Abrade / MEK 6.8 MPa (983 lb/in²) ¹

Aluminum (Alclad) N/mm² 6.7 (psi) (965)

Substrate: Aluminum … Surface Prep: Solvent Wipe … Dwell Time: 7 d … Overlap Shear Strength ASTM D1002, ISO 4587 900 lb/in² ¹

Cured for 72 hours @ 22°C, Activator 7387™ on 1 side. Lap shear strength, ISO 4587: Aluminum N/mm² 5.5 (psi) (800)

Lap Shear Strength, ISO 4587: Aluminum N/mm² 2.5 (psi) (365). Cured for 72 hours @ 21 °C.

Substrate: Aluminum. Surface Prep: Solvent Wipe. Dwell Time: 7 d. Overlap Shear Strength ASTM D1002, ISO 4587 300 lb/in².

After 7days @ 25±2 °C / 50±5 % RH and 1.0 mm gap. Lap Shear Strength, ISO 4587: Aluminum (Alclad) N/mm² ≥1.0LMS (psi) (≥145)