Acrylic adhesive on Stainless Steel
20 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE AA H8610 Stainless Steel N/mm² 28 (psi) (4,150) | not stated | 28 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS Light Abrasion and Solvent 26.2 MPa (3800 lb/in²) (CF ) 23 °C Stainless Steel | abraded | 26.2 MPa | ASTM D1002, ISO 4587 | TDS p.p3 |
| LOCTITE AA H3151 Stainless Steel 3750 | not stated | 25.86 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE AA H8600 Stainless steel N/mm² 25.7 (psi) (3,720) | not stated | 25.7 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8405NS Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. Stainless Steel, light abrasion and solvent clean, 25.5 MPa (3700 lb/in²). | abraded | 25.5 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| LOCTITE AA H3000 Stainless Steel 3540 | not stated | 24.41 MPa | ASTM D1002 | TDS p.1 |
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Light Abrasion and Solvent 24.1 MPa (3500 lb/in²) (CF) 23 °C Stainless Steel | abraded | 24.1 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Light Abrasion and Solvent 23.4 MPa (3400 lb/in²) (CF) 23 °C Stainless Steel | abraded | 23.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP810 Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Stainless Steel Light Abrasion and Solvent Clean 23 MPa (3400 lb/in²) (CF ) ¹ | abraded | 23 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 Stainless Steel N/mm² 23 (psi) (3,410) | not stated | 23 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Stainless Steel 22.8 MPa (3300 lb/in²) (CF) ¹ | abraded | 22.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Stainless Steel 22.1 MPa (3200 lb/in²) (CF) ¹ | abraded | 22.1 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2022-1 A/B Stainless steel, V4A 3,200 3,080 ASTM D1002 | degreased | 21.24 MPa | ASTM D1002 | TDS p.p3 |
| LOCTITE AA H3101 Stainless steel N/mm² 20 (psi) (2,910) | not stated | 20 MPa | ISO 4587 | TDS p.1 |
| LOCTITE AA H3410 Stainless Steel N/mm2 (psi) 20 (2,920) | not stated | 20 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Stainless Steel 19.3 MPa (2800 lb/in²) (CF) ¹ | abraded | 19.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H8010 Lap Shear Strength, ISO 4587: Stainless Steel N/mm² 18 (psi) (2,650). Cured for 72 hours @ 22 °C. | not stated | 18 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: Stainless Steel (MEK/abrade/MEK) 1990. Cured 7 days at room temperature. | abraded | 13.7206 MPa | ASTM D1002 | TDS p.3 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010 Overlap Shear Strength. Temperature: 23 °C (73 °F). Dwell Time: 7 d. Test Method: ASTM D1002, ISO 4587. Stainless Steel MEK/Abrade/MEK 1820 lb/in². (CF). | abraded | 12.5485 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA A-671 Stainless steel N/mm² 11 (psi) (1,600) | not stated | 11 MPa | ISO 4587 | TDS p.2 |