Acrylic adhesive on ABS
17 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS 9 MPa (1300 lb/in²) (SF) ¹ | abraded | 9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS 9 MPa (1300 lb/in²) (SF) ¹ | abraded | 9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: ABS 1240. Cured 7 days at room temperature. | abraded | 8.5495 MPa | ASTM D1002 | TDS p.3 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS 8.3 MPa (1200 lb/in²) (SF) ¹ | abraded | 8.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8405NS Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. ABS, light abrasion and solvent clean, 7.6 MPa (1100 lb/in²). | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C ABS 7.6 MPa (1100 lb/in²) (SF) ¹ | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C ABS 7.6 MPa (1100 lb/in²) (SF) ¹ | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS Light Abrasion and Solvent 6.9 MPa (1000 lb/in²) (SF ) 23 °C ABS | abraded | 6.9 MPa | ASTM D1002, ISO 4587 | TDS p.p2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8710NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 24 h 23 °C ABS 5.8 MPa (846 lb/in²) ¹ | abraded | 5.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8610NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … ABS Solvent Wipe (IPA) 5.6 MPa (807 lb/in²) ¹ | degreased | 5.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … ABS Solvent Wipe (IPA) 5.6 MPa (813 lb/in²) ¹ | degreased | 5.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8910NS Overlap Shear Strength, dwell 7 d, ASTM D1002, ISO 4587. ABS, IPA Wipe/Abrade/IPA Wipe, 4.4 MPa (635 lb/in²). | abraded | 4.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP810 Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … ABS Solvent Wipe 4.1 MPa (600 lb/in²) (MM ) ¹ | degreased | 4.1 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8705NS Overlap Shear Strength … Test Condition: 23 °C … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … ABS Light Abrasion and Solvent Clean 3.5 MPa (505 lb/in²) ² | abraded | 3.5 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2022-1 A/B ABS 480 (substrate failure) 500 (substrate failure) ASTM D1002 | abraded | 3.45 MPa | ASTM D1002 | TDS p.p3 |
| LOCTITE AA H8610 ABS N/mm² 3 (psi) (480) | not stated | 3 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 ABS N/mm² 2 (psi) (260) | not stated | 2 MPa | ISO 4587 | TDS p.2 |