Acrylic adhesive on Fiberglass
18 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin Light Abrasion and Solvent 23 °C 29 MPa (4200 lb/in²) (CF) ¹ (fiber-reinforced) | abraded | 29 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS Epoxy Resin Light Abrasion and Solvent 28.3 MPa (4100 lb/in²) (SF ) | abraded | 28.3 MPa | ASTM D1002, ISO 4587 | TDS p.p2 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin Light Abrasion and Solvent 22.8 MPa (3300 lb/in²) (CF) 23 °C (fiber-reinforced) | abraded | 22.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin (fiber-reinforced) 22.8 MPa (3300 lb/in²) (CF) ¹ | abraded | 22.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin (fiber-reinforced) 20.7 MPa (3000 lb/in²) (CF) ¹ | abraded | 20.7 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin (fiber-reinforced) 20 MPa (2900 lb/in²) (CF) ¹ | abraded | 20 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8710NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin Light Abrasion and 13.4 MPa (1948 lb/in²) 24 h 23 °C (fiber-reinforced) | abraded | 13.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8705NS Overlap Shear Strength … Test Condition: 23 °C … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin (fiber-reinforced) Light Abrasion and Solvent Clean 11.7 MPa (1701 lb/in²) ² | abraded | 11.7 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H3000 Gelcoat 1490 | not stated | 10.27 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE AA H8010 Lap Shear Strength, ISO 4587: FRP N/mm² 10 (psi) (1,425). Cured for 72 hours @ 22 °C. | not stated | 10 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H3151 Gelcoat >1440 | not stated | > 9.93 MPa | ASTM D1002 | TDS p.1 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8725NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … Epoxy Resin Light Abrasion and 9.9 MPa (1435 lb/in²) 24 h 23 °C (fiber-reinforced) | abraded | 9.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H3101 Gelcoat N/mm² 8.6 (psi) (1,255) | not stated | 8.6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE AA H8500 Gelcoat N/mm² 6 (psi) (850) | not stated | 6 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Polyester resin (fiber-reinforced) MEK / Abrade / MEK 5.6 MPa (809 lb/in²) ¹ | abraded | 5.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8610NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Polyester resin (fiber-reinforced) MEK / Abrade / MEK 5.2 MPa (755 lb/in²) ¹ | abraded | 5.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA 3751 Cured @ 30 mW/cm², measured @ 365 nm, for 2 minutes using a Zeta® 7400 light source Lap Shear Strength, ISO 4587: Epoxyglass N/mm² ≥5.2 | not stated | > 5.2 MPa | ISO 4587 | TDS p.1 |
| LOCTITE AA H8610 Gelcoat N/mm² 5 (psi) (790) | not stated | 5 MPa | ISO 4587 | TDS p.2 |