Acrylic adhesive on Polycarbonate
23 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE AA 3105 Lap Shear Strength, ISO 4587: Polycarbonate to Polycarbonate: Initial N/mm² 25.1 (psi) (3,640) | not stated | 25.1 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA 3201 Lap Shear Strength, ISO 4587: Polycarbonate N/mm² 11.7 (psi) (1,700) | not stated | 11.7 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA 3211 Lap Shear Strength, ISO 4587: Polycarbonate N/mm² 11 (psi) (1,600) | not stated | 11 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C Polycarbonate (PC) 9 MPa (1300 lb/in²) (SF) ¹ | abraded | 9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8405NS Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. Polycarbonate (PC), light abrasion and solvent clean, 8.3 MPa (1200 lb/in²). | abraded | 8.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C Polycarbonate (PC) 8.3 MPa (1200 lb/in²) (SF) ¹ | abraded | 8.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010 Overlap Shear Strength. Temperature: 23 °C (73 °F). Dwell Time: 7 d. Test Method: ASTM D1002, ISO 4587. Polycarbonate (PC) IPA Wipe/Abrade/IPA Wipe 1150 lb/in². (SF). | abraded | 7.929 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS Light Abrasion and Solvent 7.6 MPa (1100 lb/in²) (SF ) 23 °C Polycarbonate (PC) | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.p3 |
| ARALDITE 2022-1 A/B PC 750 (substrate failure) 990 (substrate failure) ASTM D1002 | abraded | 6.83 MPa | ASTM D1002 | TDS p.p3 |
| LOCTITE AA H3000 Polycarbonate 960 | not stated | 6.62 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE AA H3101 Polycarbonate N/mm² 6 (psi) (870) | not stated | 6 MPa | ISO 4587 | TDS p.1 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polycarbonate (PC) 5.9 MPa (850 lb/in²) (CF) ¹ | abraded | 5.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polycarbonate (PC) 5.9 MPa (850 lb/in²) (CF) ¹ | abraded | 5.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polycarbonate (PC) 5.2 MPa (750 lb/in²) (CF) ¹ | abraded | 5.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: PC 740. Cured 7 days at room temperature. | abraded | 5.1021 MPa | ASTM D1002 | TDS p.3 |
| LOCTITE AA 3751 Polycarbonate to Polycarbonate N/mm² *4.8 (psi) (700) | not stated | 4.8 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H3151 Polycarbonate 690 | not stated | 4.76 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE AA H8610 Polycarbonate N/mm² 4 (psi) (640) | not stated | 4 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8610NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Polycarbonate (PC) Solvent Wipe (IPA) 3.7 MPa (542 lb/in²) ¹ | degreased | 3.7 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Polycarbonate (PC) Solvent Wipe (IPA) 3.2 MPa (467 lb/in²) ¹ | degreased | 3.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 Polycarbonate N/mm² 3 (psi) (450) | not stated | 3 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8710NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 24 h 23 °C Polycarbonate (PC) 1.2 MPa (168 lb/in²) ¹ | abraded | 1.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8910NS Overlap Shear Strength, dwell 7 d, ASTM D1002, ISO 4587. Polycarbonate (PC), IPA Wipe/Abrade/IPA Wipe, 0.9 MPa (131 lb/in²). | abraded | 0.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |