Acrylic adhesive on PMMA
18 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS 23 °C Acrylic (PMMA) 11 MPa (1600 lb/in²) (SF ) | abraded | 11 MPa | ASTM D1002, ISO 4587 | TDS p.p2 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Light Abrasion and Solvent 10.3 MPa (1500 lb/in²) (SF) 23 °C Acrylic (PMMA) | abraded | 10.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8405NS Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. Acrylic (PMMA), light abrasion and solvent clean, 9 MPa (1300 lb/in²). | abraded | 9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C Acrylic (PMMA) 9 MPa (1300 lb/in²) (SF) ¹ | abraded | 9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: Acrylic 1190. Cured 7 days at room temperature. | abraded | 8.2048 MPa | ASTM D1002 | TDS p.3 |
| 3M Scotch-Weld Acrylic Adhesive DP810 Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) Solvent Wipe 7.6 MPa (1100 lb/in²) (SF ) ¹ | degreased | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) 7.6 MPa (1100 lb/in²) (SF) ¹ | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) 7.6 MPa (1100 lb/in²) (SF) ¹ | abraded | 7.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) 6.9 MPa (1000 lb/in²) (SF) ¹ | abraded | 6.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8910NS Overlap Shear Strength, dwell 7 d, ASTM D1002, ISO 4587. Acrylic (PMMA), IPA Wipe/Abrade/IPA Wipe, 5.4 MPa (786 lb/in²). | abraded | 5.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8610NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) Solvent Wipe (IPA) 4.8 MPa (698 lb/in²) ¹ | degreased | 4.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) Solvent Wipe (IPA) 4.6 MPa (660 lb/in²) ¹ | degreased | 4.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8705NS Overlap Shear Strength … Test Condition: 23 °C … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Acrylic (PMMA) Light Abrasion and Solvent Clean 4.2 MPa (616 lb/in²) ² | abraded | 4.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8710NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 24 h 23 °C Acrylic (PMMA) 4 MPa (582 lb/in²) ¹ | abraded | 4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2022-1 A/B PMMA 570 (substrate failure) 560 (substrate failure) ASTM D1002 | abraded | 3.86 MPa | ASTM D1002 | TDS p.p3 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8725NS Overlap Shear Strength … Temperature: 23 °C (73 °F) … Test Method: ASTM D1002, ISO 4587 … 24 h 23 °C Acrylic (PMMA) 3.7 MPa (539 lb/in²) ¹ | abraded | 3.7 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 Acrylic N/mm² 3 (psi) (430) | not stated | 3 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H8610 Acrylic N/mm² 3 (psi) (430) | not stated | 3 MPa | ISO 4587 | TDS p.2 |