Acrylic adhesive on PVC
15 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Metal Bonder Acrylic Adhesive DP8407NS Light Abrasion and Solvent 13.1 MPa (1900 lb/in²) (SF ) 23 °C Polyvinyl chloride (PVC) | abraded | 13.1 MPa | ASTM D1002, ISO 4587 | TDS p.p3 |
| 3M Scotch-Weld Acrylic Adhesive DP8405NS Overlap Shear Strength, 24 h, ASTM D1002, ISO 4587. Polyvinyl chloride (PVC), light abrasion and solvent clean, 12.4 MPa (1800 lb/in²). | abraded | 12.4 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8805NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) 12.4 MPa (1800 lb/in²) (SF) ¹ | abraded | 12.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8810NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) 12.4 MPa (1800 lb/in²) (SF) ¹ | abraded | 12.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Structural Plastic Adhesive DP8010NS Blue Overlap Shear (psi), ASTM D1002. DP8010NS Blue column: PVC 1740. Cured 7 days at room temperature. | abraded | 11.9969 MPa | ASTM D1002 | TDS p.3 |
| 3M Scotch-Weld Acrylic Adhesive DP8410NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Light Abrasion and Solvent 11.7 MPa (1700 lb/in²) (SF) 23 °C Polyvinyl chloride (PVC) | abraded | 11.7 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Acrylic Adhesive DP8425NS Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … 23 °C Polyvinyl chloride (PVC) 11 MPa (1600 lb/in²) (SF) ¹ | abraded | 11 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Low Odor Acrylic Adhesive DP8825NS Overlap Shear Strength … Surface Prep: Light Abrasion and Solvent Clean … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) 10.3 MPa (1500 lb/in²) (SF) ¹ | abraded | 10.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP810 Overlap Shear Strength … Dwell Time: 24 h … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) Solvent Wipe 6.9 MPa (1000 lb/in²) (SF ) ¹ | degreased | 6.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2022-1 A/B PVC 820 (substrate failure) 790 (substrate failure) ASTM D1002 | abraded | 5.45 MPa | ASTM D1002 | TDS p.p3 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8610NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … PVC Solvent Wipe (IPA) 4.8 MPa (691 lb/in²) ¹ | degreased | 4.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE AA H8500 PVC N/mm² 4 (psi) (540) | not stated | 4 MPa | ISO 4587 | TDS p.2 |
| LOCTITE AA H8610 PVC N/mm² 4 (psi) (590) | not stated | 4 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Flexible Acrylic Adhesive DP8625NS Overlap Shear Strength … Dwell Time: 72 h … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) Solvent Wipe (IPA) 3.6 MPa (518 lb/in²) ¹ | degreased | 3.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Acrylic Adhesive DP8910NS Overlap Shear Strength, dwell 7 d, ASTM D1002, ISO 4587. Polyvinyl chloride (PVC), IPA Wipe/Abrade/IPA Wipe, 2.9 MPa (414 lb/in²). | abraded | 2.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |