16 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE 2047 After 72 hours @22°C. Compressive shear strength, ISO 10123: Steel pins and collars N/mm2 24.5 (psi) (3,550) | not stated | 24.5 MPa | ISO 10123 | TDS p.2 |
| LOCTITE AA 3510 N/mm 23 Mild steel (grit blasted) | grit blasted | 23 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE AA 312 Steel (grit blasted) N/mm² ≥17.2LMS | grit blasted | > 17.2 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE AA 326 0.25 mm gap N/mm² 13.8 | grit blasted | 13.8 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE AA 324 0.5 mm gap N/mm² 11 | grit blasted | 11 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 243 Cured for 24 hours @ 23°C. Compressive Shear Strength, ISO 10123: Steel pins and collars N/mm2 >7.6 (psi) (1,100) | not stated | > 7.6 MPa | ISO 10123 | TDS p.2 |
| LOCTITE 232 After 2 hours @ 121 °C. Compressive Shear Strength, ISO 10123: Steel pins and collars N/mm² ≥7.0LMS (psi) (1,015) | not stated | > 7 MPa | ISO 10123 | TDS p.1 |
| LOCTITE 2432 After 24 hours @ 22 °C. Compressive Shear Strength, ISO 10123: Steel pins and collars N/mm² ≥6LMS (psi) (≥870) | not stated | > 6 MPa | ISO 10123 | TDS p.1 |
| LOCTITE 515 Cured for 24 hours @ 22 °C … Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 6.0 | grit blasted | 6 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 534 Cured for 24 hours @ 22 °C … Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² ≥4 | grit blasted | > 4 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 549 Cured for 72 hours @ 22 °C … Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 3.6 | grit blasted | 3.6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 190017 Cured for 24 hours @ 22 °C, 0.05 mm gap. Lap Shear Strength, ISO 4587: Steel N/mm² 2.8LMS (psi) (405) | not stated | 2.8 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 222 Compressive Shear Strength, ISO 10123: Steel pins and collars N/mm² ≥2.5 (psi) (≥360) | not stated | > 2.5 MPa | ISO 10123 | TDS p.2 |
| LOCTITE High Flex Gasket Maker 0.25 mm gap, 1 side activated with N/mm² 2.4 | not stated | 2.4 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 5127 Cured for 24 hours @ 22 °C … Lap Shear Strength, ISO 4587: … Steel: … 0.25 mm gap N/mm² 2.1 | not stated | 2.1 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 5127 Passivated steel: … 0.25 mm gap, 1 side activated with … Activator 7649™ … N/mm² 1.8 | primed | 1.8 MPa | ISO 4587 | TDS p.2 |