Two-part epoxy on Brass
6 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| ARALDITE 2011 A/B Average lap shear strength, metal-metal joints, sand blasting pre-treatment, psi. ISO 4587. Brass 3,481 psi | grit blasted | 24 MPa | ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Epoxy Adhesive DP460NS Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Brass MEK/Abrade/MEK 3,400 lb/in² | abraded | 23.44 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 5865 A/B Brass 0.06/1.5 2300 (15.8) | not stated | 15.86 MPa | DIN 53283 | TDS p.5 |
| LOCTITE EA 9461 Brass N/mm² 11 (psi) (1,600) | not stated | 11 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP100 Clear Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Brass MEK/Abrade/MEK 4.8 MPa (700 lb/in²) ¹ | abraded | 4.8 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP100NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Brass MEK/Abrade/MEK 500 lb/in² ¹ | abraded | 3.45 MPa | ASTM D1002, ISO 4587 | TDS p.2 |