Two-part epoxy on Stainless Steel
18 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Epoxy Adhesive DP460 Off-White Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Stainless Steel MEK/Abrade/MEK 28 MPa (4000 lb/in²) | abraded | 28 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE EA E-60HP Stainless Steel N/mm² 27 (psi) (3,900) | not stated | 27 MPa | ISO 4587 | TDS p.1 |
| LOCTITE PC 7210 Lap Shear Strength ISO 4587: Stainless steel (grit blasted) N/mm² 27. Cured for 7 days @ 22°C. | grit blasted | 27 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP490 Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method Test Condition Substrate Surface Prep Value … ASTM D1002, ISO 4582 Stainless Steel Sandblasted 24 MPa (3481 lb/in²) (CF ) | grit blasted | 24 MPa | ASTM D1002, ISO 4582 | TDS p.2 |
| LOCTITE EA M-121HP Stainless steel N/mm² 23.1 (psi) (3,350) | not stated | 23.1 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive 6101 Overlap Shear Strength … Test Condition: 1 hr at 65 °C + 24 hr at 23 °C … Test Method: ASTM D1002, ISO 4587 … Stainless Steel 23 MPa (Adhesive Failure ) ² | grit blasted | 23 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| LOCTITE EA E-120HP Stainless steel N/mm² 23 (psi) (3,400) | not stated | 23 MPa | ISO 4587 | TDS p.2 |
| ARALDITE 5865 A/B Stainless Steel 0.039/1.0 3200 (22) | not stated | 22.06 MPa | DIN 53283 | TDS p.5 |
| ARALDITE 2011 A/B Average lap shear strength, metal-metal joints, sand blasting pre-treatment, psi. ISO 4587. Stainless Steel 3,191 psi | grit blasted | 22 MPa | ISO 4587 | TDS p.3 |
| LOCTITE EA E-20HP Stainless Steel N/mm² 22.0 (psi) (3,190) | not stated | 22 MPa | ISO 4587 | TDS p.1 |
| LOCTITE AA H4500 Lap Shear Strength, ISO 4587: Stainless Steel N/mm² 20.7 (psi) (3,000) | not stated | 20.7 MPa | ISO 4587 | TDS p.2 |
| LOCTITE EA 9461 Stainless steel N/mm² 19 (psi) (2,800) | not stated | 19 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP460NS Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Stainless Steel MEK/Abrade/MEK 2,400 lb/in² | abraded | 16.55 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE EA M-31CL Stainless steel N/mm² 13.6 (psi) (1,970) | not stated | 13.6 MPa | ISO 4587 | TDS p.2 |
| LOCTITE EA E-00CL/100CL Stainless steel N/mm² 13 (psi) (1,900) | not stated | 13 MPa | ISO 4587 | TDS p.2 |
| LOCTITE EA E-90FL Stainless Steel N/mm² 6.7 (psi) (970) | not stated | 6.7 MPa | ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP100NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Stainless Steel MEK/Abrade/MEK 840 lb/in² ¹ | abraded | 5.79 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP100 Clear Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Stainless Steel MEK/Abrade/MEK 5.2 MPa (750 lb/in²) ¹ | abraded | 5.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |