Two-part epoxy on Steel

Lap Shear Strength ISO 4587: Mild Steel (grit Blasted) N/mm² 35. Cured for 7 days @ 22°C.

Cured @ 65°C for 12 hours Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 30 (psi) (4,300)

Cured for 5 days @ 23 °C Lap Shear Strength, ISO 4587: Mild Steel (Grit Blasted) N/mm² 30 (psi) (4,300)

Cured @ 65°C for 12 hours Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 29.4 (psi) (4,270)

Tensile lap-shear strength (CQP046-9 / ISO 4587) 28 MPa (4050 psi) C, D, E

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method Test Condition Substrate Surface Prep Value … ASTM D1002, ISO 4583 Steel DD11 Sandblasted 27 MPa (3916 lb/in²) (CF )

Lap Shear Strength, ISO 4587 Mild steel (grit blasted) N/mm² 25 (psi) (3600)

Cured for 7days @ 22°C Lap Shear Strength, ISO 4587: Mild steel (grit blasted) N/mm² 25 (psi) (3,600)

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Cold Rolled Steel MEK/Abrade/MEK 3,600 lb/in²

CR Steel, MEK wiped, test temp 77 °F, typical value 3500

Grit Blasted Mild Steel (GBMS) N/mm² 23.9

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Galvanized Steel MEK/Abrade/MEK 3400 lb/in² (CF/AF )

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Galvanized Steel MEK/Abrade/MEK 3400 lb/in² (CF/AF )

Cured for 5 days @ 23°C Lap Shear Strength ISO 4587: Mild Steel (Grit Blasted) N/mm² 22.6 (psi) (3,270)

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Galvanized Steel MEK/Abrade/MEK 3210 lb/in² (CF )

Adhesive Lap Shear (GBS) 3,200 psi (22 MPa)

Cured for 5 days @22°C Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 21.4 (psi) (3,100)

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 20.8 MPa (3010 lb/in²)

CR Steel Abraded, test temp 77 °F, typical value 3000 psi

CR Steel Degreased, test temp 77 °F, typical value 2850 psi

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 19.6 MPa (2840 lb/in²)

Lap Shear Strength, ISO 4587: Mild steel (grit blasted) N/mm² 19.5 (psi) (2,820)

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Cold Rolled Steel MEK/Abrade/MEK 19 MPa (2800 lb/in²)

Adhesive Lap Shear (GBS) 2,750 psi (19 MPa)

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 18.8 MPa (2730 lb/in²)

Grit Blasted Mild Steel (GBMS) N/mm² 18.4

Average lap shear strength, metal-metal joints, sand blasting pre-treatment, psi. ISO 4587. Galvanized steel 2,611 psi

Adhesive Lap Shear (GBS) 2,680 psi (18.0 Mpa)

CR Steel Oily, test temp 77 °F, typical value 2600 psi

Adhesive Tensile Lap Shear (GBS) 2,600 psi (17.9 Mpa)

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 17.8 MPa (2580 lb/in²)

Carbon Steel 0.039/1.0 2500 (17.2)

Adhesive Lap Shear (GBS) 2,500 psi (17.2 MPa). Standard test: Tensile Lap Shear ASTM D1002. Cured 7 Days @ 75°F (24°C).

Substrate: Cold Rolled Steel … Surface Prep: MEK/Abrade/MEK … Dwell Time: 7 d … Overlap Shear Strength ASTM D1002, ISO 4587 17.2 MPa (2500 lb/in²) ¹

Adhesive Lap Shear (GBS) 2,400 psi (16.55 MPa)

Substrate: Cold Rolled Steel … Surface Prep: MEK/Abrade/MEK … Dwell Time: 7 d … Overlap Shear Strength ASTM D1002, ISO 4587 2,400 lb/in² ¹

Shear Strength, ASTM D 1002 Cured 5 Days @ 77 °F. Bonderized Steel, test temp 77 °F, typical value 2400 psi

Substrate: Steel … Surface Prep: Solvent Wipe … Dwell Time: 7 d … Overlap Shear Strength ASTM D1002, ISO 4587 16.5 MPa (2400 lb/in²) ¹

Galvanized Steel (Hot Dipped) N/mm² 16 (psi) (2,300)

Adhesive Lap Shear (GBS) 2,250 psi (15.5 MPa)

Substrate: Cold Rolled Steel … Surface Prep: MEK/Abrade/MEK … Dwell Time: 7 d … Overlap Shear Strength ASTM D1002, ISO 4587 2,200 lb/in² ¹

Cured for 30 minutes @ 150 °C. Lap Shear Strength, ISO 4587: Mild steel (grit blasted) N/mm² ≥15 LMS (psi) (≥2,175)

Lap Shear Strength, ISO 4587: Galvanized Steel N/mm² 15 (psi) (2,140)

Cured for 5 days @ 22 °C Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 15 (psi) (2,200)

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 14.3 MPa (2080 lb/in²)

Grit Blasted Mild Steel (GBMS) N/mm² 13.9

Adhesive Tensile Shear (GBS) 2,000 psi (13.8 MPa)

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Test Condition Substrate Surface Prep Value … CRS Acetone/Abrade/Acetone 13.5 MPa (1960 lb/in²)

Lap Shear Strength, ISO 4587: Grit Blasted Mild Steel (GBMS) N/mm² 13.5 (psi) (1,955)

Adhesive Lap Shear (GBS) 1,900 psi (13.1 MPa). Standard test: Tensile Lap Shear ASTM D1002. Cured 7 Days @ 75°F (24°C).

Lap Shear Strength, ISO 4587: Grit Blasted Mild Steel (GBMS) N/mm² 12.4 (psi) (1,800)

Adhesive Lap Shear (GBS) 1,600 psi (11.0 MPa)

Lap Shear Strength, ISO 4587: Grit Blasted Mild Steel (GBMS) N/mm² 11 (psi) (1,610)

Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² ≥10.3LMS (psi) (≥1,493)

Adhesive Lap Shear (GBS) 1,450 psi (10.0 MPa)

Cured for 30 minutes @ 150 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² ≥10 LMS (psi) (≥1,450)

Galvanized Steel1 0.06/1.5 1300 (8.9)

Overlap Shear Strength … Surface Prep: MEK/Abrade/MEK … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Cold Rolled Steel 8 MPa (1100 lb/in²) ¹

Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Galvanized Steel MEK/Abrade/MEK 1,080 lb/in² ¹

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 7.2 MPa (1050 lb/in²)

Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d CRS Acetone/Abrade/Acetone 7.0 MPa (1010 lb/in²)

Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Galvanized Steel MEK/Abrade/MEK 6.2 MPa (900 lb/in²) ¹

Cured for 5 days @ 22°C Lap Shear Strength ISO 4587: Steel (grit blasted) N/mm² 5.6 (psi) (810)

Lap Shear Strength, ISO 4587: Mild steel (grit blasted) N/mm² 3.8 (psi) (550)

Grit Blasted Mild Steel (GBMS) N/mm² 3.4

Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Test Condition Substrate Surface Prep Value … CRS Acetone/Abrade/Acetone 0.6 MPa (90 lb/in²)