Two-part epoxy on PVC
15 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Epoxy Adhesive DP125 Translucent Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 4.9 MPa (710 lb/in²) | abraded | 4.9 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP125 Gray Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 4.5 MPa (650 lb/in²) | abraded | 4.5 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP460 Off-White Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 3.4 MPa (500 lb/in²) | abraded | 3.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP190 Translucent Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 3.2 MPa (460 lb/in²) | abraded | 3.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP270 Clear Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Test Condition Substrate Surface Prep Value … 23 °C Polyvinyl chloride (PVC) Solvent Wipe 2.4 MPa (350 lb/in²) | degreased | 2.4 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Epoxy Adhesive DP100 Clear Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 2.3 MPa (330 lb/in²) ¹ | abraded | 2.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP460NS Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Substrate Surface Prep Value … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 313 lb/in² | abraded | 2.16 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP270 Black Overlap Shear Strength Temperature: 23 °C (73 °F) Dwell Time: 7 d Test Method: ASTM D1002, ISO 4587 Test Condition Substrate Surface Prep Value … 23 °C Polyvinyl chloride (PVC) Solvent Wipe 2.0 MPa (290 lb/in²) | degreased | 2 MPa | ASTM D1002, ISO 4587 | TDS p.3 |
| ARALDITE 2011 A/B Average lap shear strength, plastic-plastic joints, lightly abrade and alcohol degrease pre-treatment, psi. ISO 4587. PVC 290 psi | abraded | 2 MPa | ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Epoxy Adhesive DP100NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 240 lb/in² ¹ | abraded | 1.65 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE EA 9462 PVC, test temp 77 °F, typical value 225 | not stated | 1.55 MPa | ASTM D1002 | TDS p.1 |
| 3M Scotch-Weld Epoxy Adhesive DP420NS Black Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 1.5 MPa (220 lb/in²) | abraded | 1.5 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP420 Off-White Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 1.4 MPa (200 lb/in²) | abraded | 1.4 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP420 Black Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 1.2 MPa (180 lb/in²) | abraded | 1.2 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Epoxy Adhesive DP405 Overlap Shear Strength Temperature: 23 °C (73 °F) Test Method: ASTM D1002, ISO 4587 Dwell Time Substrate Surface Prep Value … 7 d Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 1 MPa (140 lb/in²) | abraded | 1 MPa | ASTM D1002, ISO 4587 | TDS p.2 |