Ethyl cyanoacrylate on Aluminum
41 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE 402 Lap Shear Strength ISO 4587: … Aluminum (etched) N/mm2 (psi) 20 | etched | 20 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Instant Tough Black MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … Aluminium A5754 [N/mm2 ] 18 - 22 | not stated | 18–22 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 380 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 18 | etched | 18 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 438 Aluminum N/mm² 18 | not stated | 18 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 17.3 | etched | 17.3 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 454 Aluminum (etched) N/mm² 17.1 | etched | 17.1 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 455 Aluminum (etched) N/mm² 16.2 | etched | 16.2 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE Super Glue Ultra Liquid Control Tensile Shear Strength ISO 4587, 12-24 hours cure. Aluminum: 2248 psi (15.5 N/mm²). | not stated | 15.4994 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 410 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 15 | etched | 15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 5019H Aluminum (grit blasted) N/mm² 15 to 19 | grit blasted | 15–19 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4205 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum N/mm² 14.5 | not stated | 14.5 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Instant Tough MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … Aluminium A5754 [N/mm2 ] 14 - 18 | not stated | 14–18 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm 2 (psi) 12.4 | etched | 12.4 MPa | ISO 4587 | TDS p.2 |
| MG 8334 Lap Shear Strength ISO 4587: Stainless Steel >14.5; Aluminum >12.1; ABS >6.2; PVC >6.2; Polycarbonate >6.2; Neoprene >5.2 N/mm². Sample cured at 50% RH for at least 24 hours. Coupon prep not stated. | not stated | > 12.1 MPa | ISO 4587 lap shear | TDS p.2 |
| Born2Bond Aquafast Lap shear strength (ISO 4587) @ 23°C (MPa). After 24h Curing at RT. Aluminum (A5754) 13 +/- 1. | not stated | 12–14 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 406 Lap Shear Strength, ISO 4587: Aluminum (etched) N/mm² 12 (psi) (1,740). After 24 hours @ 22 °C. | etched | 12 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm 2 (psi) 12 | etched | 12 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 12 to 19 | etched | 12–19 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (grit blasted) N/mm² 12 to 19 | grit blasted | 12–19 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (grit blasted) N/mm² 12 to 19 | grit blasted | 12–19 MPa | ISO 4587 | TDS p.2 |
| Born2Bond MP515 Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa) After 24 hours curing @ RT … Aluminum (A5754) 12 +/- 1 | not stated | 11–13 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Structural Lap shear strength (ISO 4587) @ 23°C (MPa). After 24 hours curing @ RT. Aluminum (A5754) 12 +/- 1. | not stated | 11–13 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 382 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 11 to 19 | etched | 11–19 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 404 Lap Shear Strength, ISO 4587: Aluminum (etched) N/mm² 11 to 19. After 24 hours @ 22 °C. | etched | 11–19 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 411 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm² 11 to 19 | etched | 11–19 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4471 Aluminum (etched) N/mm² 11 to 19 | etched | 11–19 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4541 Aluminum (etched) N/mm² 11 to 19 | etched | 11–19 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 499 Aluminum N/mm² 11 to 19 | not stated | 11–19 MPa | ISO 4587 | TDS p.p1 |
| Loctite 414 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength: Steel (grit blasted) 18 to 26 N/mm²; Aluminum (etched) 11 to 19 N/mm²; ABS >6; PVC >4; Polycarbonate >5; Phenolic 5 to 15; Neoprene >10; Nitrile >10 N/mm². | etched | 11–19 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 495 Aluminum (grit blasted) N/mm² 10.8 | grit blasted | 10.8 MPa | ISO 4587 | TDS p.p1 |
| Loctite 495 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) 14.2 N/mm²; Aluminum (grit blasted) 10.8 N/mm²; ABS 7.9; PVC 8.7; Polycarbonate 8; Phenolic 9.9; Neoprene 1; Nitrile 1.3 N/mm². | grit blasted | 10.8 MPa | ISO 4587 lap shear | TDS p.1 |
| Gorilla Super Glue Aluminum > 1500 psi ASTM D1002 | not stated | > 10.34 MPa | ASTM D1002 | TDS p.p1 |
| Gorilla Super Glue Brush & Nozzle Aluminum > 1500 psi ASTM D1002 | not stated | > 10.34 MPa | ASTM D1002 | TDS p.p1 |
| Gorilla Super Glue Gel Aluminum > 1500 psi ASTM D1002 | not stated | > 10.34 MPa | ASTM D1002 | TDS p.p1 |
| LOCTITE 4851 Aluminum (grit blasted) N/mm² 10 to 14 | grit blasted | 10–14 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … Aluminum (etched) N/mm2 (psi) 9 to 15 | etched | 9–15 MPa | ISO 4587 | TDS p.2 |
| Permatex Super Glue Aluminum* 1200 – 1600 | grit blasted | 8.27–11.03 MPa | ASTM D1002 | TDS p.p1 |
| LOCTITE 4861 Aluminum (grit blasted) N/mm² 8 to 12 | grit blasted | 8–12 MPa | ISO 4587 | TDS p.p2 |
| SikaFast-2590 AlMg3 5 MPa C | not stated | 5 MPa | ISO 4587 | TDS p.p2 |
| Born2Bond Repair Lap shear strength (ISO 4587) @ 23°C (MPa). after 24 hours curing @ RT. Aluminum (A5754) 3 +/- 1. | not stated | 2–4 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 4206 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Aluminum N/mm² 1.0 to 1.5 | not stated | 1–1.5 MPa | ISO 4587 | TDS p.1 |