Ethyl cyanoacrylate on Steel
43 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE 380 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 26 | grit blasted | 26 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 402 Lap Shear Strength ISO 4587: … Mild Steel (Grit Blasted) N/mm2 (psi) 22 | grit blasted | 22 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 410 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 22 | grit blasted | 22 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 454 Steel (grit blasted) N/mm² 20.9 | grit blasted | 20.9 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 20.8 | grit blasted | 20.8 MPa | ISO 4587 | TDS p.2 |
| LOCTITE QuickTite Gel Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 20.2 (psi) (2,930). Cured for 24 hours @ 22 °C. | grit blasted | 20.2 MPa | ISO 4587 | TDS p.1 |
| EVERBUILD STICK2 Superglue HV Shear Strength >20Nmm² (steel-steel ASTM D1002) | not stated | > 20 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm 2 (psi) 20 | grit blasted | 20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4205 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18.7 to 23.2 | grit blasted | 18.7–23.2 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Aquafast Lap shear strength (ISO 4587) @ 23°C (MPa). After 1 Week Curing at RT. Grit-Blasted Mild Steel (GBMS) 20 +/- 2. | grit blasted | 18–22 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Instant Tough Black MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … Grit Blasted Mild steel (GBMS) [N/mm2 ] 18 - 24 | grit blasted | 18–24 MPa | ISO 4587 | TDS p.2 |
| Born2Bond Instant Tough MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … Grit Blasted Mild steel (GBMS) [N/mm2 ] 18 - 24 | grit blasted | 18–24 MPa | ISO 4587 | TDS p.1 |
| Born2Bond MP515 Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa) After 24 hours curing @ RT … Grit-Blasted Mild Steel (GBMS) 19 +/- 1 | grit blasted | 18–20 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 382 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 404 Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 18 to 26. After 24 hours @ 22 °C. | grit blasted | 18–26 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 411 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4541 Steel (grit blasted) N/mm² 18 to 26 | grit blasted | 18–26 MPa | ISO 4587 | TDS p.p2 |
| Loctite 414 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength: Steel (grit blasted) 18 to 26 N/mm²; Aluminum (etched) 11 to 19 N/mm²; ABS >6; PVC >4; Polycarbonate >5; Phenolic 5 to 15; Neoprene >10; Nitrile >10 N/mm². | grit blasted | 18–26 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 426 Cured for 48 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² ≥16.5 | grit blasted | > 16.5 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 406 Lap Shear Strength, ISO 4587: Steel (grit blasted) N/mm² 15.5 (psi) (2,250). After 24 hours @ 22 °C. | grit blasted | 15.5 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm 2 (psi) 15.5 | grit blasted | 15.5 MPa | ISO 4587 | TDS p.1 |
| EVERBUILD STICK2 Superglue GP Shear Strength 15-20 N/mm2 (steel-steel ASTM D1002) | not stated | 15–20 MPa | ASTM D1002 | TDS p.2 |
| LOCTITE 438 Steel (grit blasted) N/mm² ≥15LMS | grit blasted | > 15 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 495 Steel (grit blasted) N/mm² 14.2 | grit blasted | 14.2 MPa | ISO 4587 | TDS p.p1 |
| Loctite 495 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) 14.2 N/mm²; Aluminum (grit blasted) 10.8 N/mm²; ABS 7.9; PVC 8.7; Polycarbonate 8; Phenolic 9.9; Neoprene 1; Nitrile 1.3 N/mm². | grit blasted | 14.2 MPa | ISO 4587 lap shear | TDS p.1 |
| LOCTITE 4206 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm² 14.1 to 16.7 | grit blasted | 14.1–16.7 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Repair Lap shear strength (ISO 4587) @ 23°C (MPa). After 1 week Curing at RT. Grit-Blasted Mild Steel (GBMS) 15 +/- 1. | grit blasted | 14–16 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Structural Lap shear strength (ISO 4587) @ 23°C (MPa). After 1 week curing @ RT. Steel (grit-blasted) 15 +/- 1. | grit blasted | 14–16 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … Steel (grit blasted) N/mm2 (psi) 14 to 22 | grit blasted | 14–22 MPa | ISO 4587 | TDS p.2 |
| Permatex Super Glue Steel* 1800 –2400 | grit blasted | 12.41–16.55 MPa | ASTM D1002 | TDS p.p1 |
| LOCTITE 4851 Steel (grit blasted) N/mm² 11 to 15 | grit blasted | 11–15 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4861 Steel (grit blasted) N/mm² 11 to 17 | grit blasted | 11–17 MPa | ISO 4587 | TDS p.p2 |
| Gorilla Super Glue Lap Shear Strength Steel > 1500 psi Aluminum > 1500 psi ASTM D1002 Polycarbonate > 800 psi EDPM > 500 psi … Fixture Time (1 drop/in2) 10-45 s | not stated | > 10.34 MPa | ASTM D1002 | TDS p.1 |
| Gorilla Super Glue Brush & Nozzle Lap Shear Strength Steel > 1500 psi Aluminum > 1500 psi ASTM D1002 Polycarbonate > 800 psi EDPM > 500 psi … Fixture Time (1 drop/in2) 10-45 s | not stated | > 10.34 MPa | ASTM D1002 | TDS p.1 |
| Gorilla Super Glue Gel Lap Shear Strength Steel > 1500 psi Aluminum > 1500 psi ASTM D1002 Polycarbonate > 800 psi EDPM > 500 psi … Fixture Time (1 drop/in2) 10-45 s | not stated | > 10.34 MPa | ASTM D1002 | TDS p.1 |
| LOCTITE 455 Steel (grit blasted) N/mm² ≥9.7LMS | grit blasted | > 9.7 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 499 Steel (grit blasted) N/mm² ≥9.0LMS | grit blasted | > 9 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4471 Steel (grit blasted) N/mm² ≥5.2LMS | grit blasted | > 5.2 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 498 Steel (grit blasted) N/mm² ≥4.8LMS | grit blasted | > 4.8 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4981 Steel (grit blasted) N/mm² ≥4.8LMS | grit blasted | > 4.8 MPa | ISO 4587 | TDS p.p1 |