Ethyl cyanoacrylate on Zinc
17 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE 406 Lap Shear Strength, ISO 4587: Zinc dichromate N/mm² 14 (psi) (2,030). After 24 hours @ 22 °C. | not stated | 14 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm 2 (psi) 14 | not stated | 14 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 454 Zinc dichromate N/mm² 11.5 | not stated | 11.5 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 499 Zinc dichromate N/mm² 8 to 15 | not stated | 8–15 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4861 Zinc dichromate N/mm² 7 to 11 | not stated | 7–11 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm² 6 to 13 | not stated | 6–13 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm² 6 to 13 | not stated | 6–13 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm² 6 to 13 | not stated | 6–13 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4471 Zinc dichromate N/mm² 6 to 10 | not stated | 6–10 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4851 Zinc dichromate N/mm² 6 to 12 | not stated | 6–12 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 495 Zinc dichromate N/mm² 5.9 | not stated | 5.9 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 402 Lap Shear Strength ISO 4587: … Zinc dichromate N/mm2 (psi) 4.5 | not stated | 4.5 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm2 (psi) 4 to 10 | not stated | 4–10 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4541 Zinc dichromate N/mm² 4 to 10 | not stated | 4–10 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm 2 (psi) 2.5 | not stated | 2.5 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 455 rials Zinc dichromate N/mm² 2.2 | not stated | 2.2 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Zinc dichromate N/mm² 2.0 | not stated | 2 MPa | ISO 4587 | TDS p.2 |