Ethyl cyanoacrylate on ABS
33 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² 9.7 | not stated | 9.7 MPa | ISO 4587 | TDS p.2 |
| Born2Bond Instant Tough Black MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … ABS [N/mm2 ] 9 - 11 * | not stated | 9–11 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 406 Lap Shear Strength, ISO 4587: ABS * N/mm² 8.8 * (psi) (1,280). After 24 hours @ 22 °C. * substrate failure. | not stated | 8.8 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … ABS N/mm 2 (psi) 8.8* | not stated | 8.8 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 454 ABS * N/mm² 8.3 | not stated | 8.3 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 402 Lap Shear Strength ISO 4587: … ABS N/mm2 (psi) 8 | not stated | 8 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 495 ABS * N/mm² 7.9 | not stated | 7.9 MPa | ISO 4587 | TDS p.p1 |
| Loctite 495 After 24 hours @ 22 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) 14.2; Aluminum (grit blasted) 10.8; ABS 7.9; PVC 8.7; Polycarbonate 8; Phenolic 9.9; Neoprene 1; Nitrile 1.3 N/mm² (* substrate failure where marked). | not stated | 7.9 MPa | ISO 4587 lap shear | TDS p.1 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … ABS N/mm 2 (psi) 7.5* | not stated | 7.5 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4851 ABS N/mm² 7 to 9 | not stated | 7–9 MPa | ISO 4587 | TDS p.p2 |
| MG 8334 Lap Shear Strength ISO 4587: Stainless Steel >14.5; Aluminum >12.1; ABS >6.2; PVC >6.2; Polycarbonate >6.2; Neoprene >5.2 N/mm². Sample cured at 50% RH for at least 24 hours. Coupon prep not stated. | not stated | > 6.2 MPa | ISO 4587 lap shear | TDS p.2 |
| LOCTITE 380 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 382 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … ABS N/mm2 (psi) 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 404 Lap Shear Strength, ISO 4587: ABS N/mm² >6. After 24 hours @ 22 °C. | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 410 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 411 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4541 ABS N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 499 ABS N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.p1 |
| Loctite 414 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength: Steel (grit blasted) 18 to 26 N/mm²; Aluminum (etched) 11 to 19 N/mm²; ABS >6; PVC >4; Polycarbonate >5; Phenolic 5 to 15; Neoprene >10; Nitrile >10 N/mm². | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Aquafast Lap shear strength (ISO 4587) @ 23°C (MPa). After 24h Curing at RT. ABS 6 +/- 1. | not stated | 5–7 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Instant Tough MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … ABS [N/mm2 ] 5 - 13 * | not stated | 5–13 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Structural Lap shear strength (ISO 4587) @ 23°C (MPa). After 24 hours curing @ RT. ABS 6 +/- 1. | not stated | 5–7 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 4861 ABS N/mm² 5 to 9 | not stated | 5–9 MPa | ISO 4587 | TDS p.p2 |
| SikaFast-2590 ABS 5 MPa S | not stated | 5 MPa | ISO 4587 | TDS p.p2 |
| Born2Bond MP515 Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa) After 24 hours curing @ RT … ABS 5 +/- 1 SF* | not stated | 4–6 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Repair Lap shear strength (ISO 4587) @ 23°C (MPa). after 24 hours curing @ RT. ABS 5 +/- 1. | not stated | 4–6 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 4471 ABS N/mm² 4 to 8 | not stated | 4–8 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 455 ABS * N/mm² 4.0 | not stated | 4 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4206 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … ABS N/mm² 3.3 to 3.9 | not stated | 3.3–3.9 MPa | ISO 4587 | TDS p.1 |