Ethyl cyanoacrylate on Phenolic Resin
31 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| Born2Bond MP515 Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa) After 24 hours curing @ RT … Phenolic 14 +/- 1 | not stated | 13–15 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … Phenolic N/mm 2 (psi) 12.6* | not stated | 12.6 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 454 Phenolic * N/mm² 12.3 | not stated | 12.3 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 406 Lap Shear Strength, ISO 4587: Phenolic * N/mm² 11.3 * (psi) (1,640). After 24 hours @ 22 °C. * substrate failure. | not stated | 11.3 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … Phenolic N/mm 2 (psi) 11.3* | not stated | 11.3 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Instant Tough Black MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … Phenolic [N/mm2 ] 11 - 14 * | not stated | 11–14 MPa | ISO 4587 | TDS p.2 |
| Born2Bond Aquafast Lap shear strength (ISO 4587) @ 23°C (MPa). After 24h Curing at RT. Phenolic 11 +/- 1. | not stated | 10–12 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 380 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 10 | not stated | 10 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 402 Lap Shear Strength ISO 4587: … Phenolic N/mm2 (psi) 10 | not stated | 10 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 410 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 10 | not stated | 10 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 498 ped Phenolic N/mm² 10 | not stated | 10 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 4981 the Phenolic N/mm² 10 | not stated | 10 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 495 Phenolic N/mm² 9.9 | not stated | 9.9 MPa | ISO 4587 | TDS p.p1 |
| Loctite 495 After 24 hours @ 22 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) 14.2; Aluminum (grit blasted) 10.8; ABS 7.9; PVC 8.7; Polycarbonate 8; Phenolic 9.9; Neoprene 1; Nitrile 1.3 N/mm² (* substrate failure where marked). | not stated | 9.9 MPa | ISO 4587 lap shear | TDS p.1 |
| LOCTITE 4205 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 8.6 to 9.5 | not stated | 8.6–9.5 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4206 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 8.6 to 9.5 | not stated | 8.6–9.5 MPa | ISO 4587 | TDS p.1 |
| Born2Bond Structural Lap shear strength (ISO 4587) @ 23°C (MPa). After 24 hours curing @ RT. Phenolic 8 +/- 1. | not stated | 7–9 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Repair Lap shear strength (ISO 4587) @ 23°C (MPa). after 24 hours curing @ RT. Phenolic 7 +/- 1. | not stated | 6–8 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 382 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … Phenolic N/mm2 (psi) 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 404 Lap Shear Strength, ISO 4587: Phenolic N/mm² 5 to 15. After 24 hours @ 22 °C. | not stated | 5–15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 411 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4471 Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4541 Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 499 Phenolic N/mm² 5 to 15 | not stated | 5–15 MPa | ISO 4587 | TDS p.p2 |
| Loctite 414 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength: Steel (grit blasted) 18 to 26 N/mm²; Aluminum (etched) 11 to 19 N/mm²; ABS >6; PVC >4; Polycarbonate >5; Phenolic 5 to 15; Neoprene >10; Nitrile >10 N/mm². | not stated | 5–15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 455 Phenolic * N/mm² 3.9 | not stated | 3.9 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … Phenolic N/mm² 1.3 | not stated | 1.3 MPa | ISO 4587 | TDS p.2 |