Ethyl cyanoacrylate on PVC
31 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| Born2Bond Instant Tough Black MV Tensile Shear strength (ISO 4587) - Cured 24 h @ 23°C Substrate … PVC [N/mm2 ] 12 - 15 * | not stated | 12–15 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4011 S Cured for 72 hours @ 22°C Tensile strength, ISO 6922 Buna-N N/mm 2 (psi) 13.7 (1,900) TDS LOCTITE® 4011 S, May 2025 Lap Shear Strength, ISO 4587: … PVC N/mm 2 (psi) 10* | not stated | 10 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 406 Lap Shear Strength, ISO 4587: PVC * N/mm² 8.7 * (psi) (1,260). After 24 hours @ 22 °C. * substrate failure. | not stated | 8.7 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4061 S After 24 hours @ 22°C Lap Shear Strength, ISO 4587: … PVC N/mm 2 (psi) 8.7* | not stated | 8.7 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 495 PVC * N/mm² 8.7 | not stated | 8.7 MPa | ISO 4587 | TDS p.p1 |
| Loctite 495 After 24 hours @ 22 °C. Lap Shear Strength, ISO 4587: Steel (grit blasted) 14.2; Aluminum (grit blasted) 10.8; ABS 7.9; PVC 8.7; Polycarbonate 8; Phenolic 9.9; Neoprene 1; Nitrile 1.3 N/mm² (* substrate failure where marked). | not stated | 8.7 MPa | ISO 4587 lap shear | TDS p.1 |
| LOCTITE 454 PVC * N/mm² 7.1 | not stated | 7.1 MPa | ISO 4587 | TDS p.p2 |
| Born2Bond MP515 Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa) After 24 hours curing @ RT … PVC 8 +/- 1 SF* | not stated | 7–9 MPa | ISO 4587 | TDS p.3 |
| Born2Bond Repair Lap shear strength (ISO 4587) @ 23°C (MPa). after 24 hours curing @ RT. PVC 8 +/- 1. | not stated | 7–9 MPa | ISO 4587 | TDS p.3 |
| MG 8334 Lap Shear Strength ISO 4587: Stainless Steel >14.5; Aluminum >12.1; ABS >6.2; PVC >6.2; Polycarbonate >6.2; Neoprene >5.2 N/mm². Sample cured at 50% RH for at least 24 hours. Coupon prep not stated. | not stated | > 6.2 MPa | ISO 4587 lap shear | TDS p.2 |
| Born2Bond Aquafast Lap shear strength (ISO 4587) @ 23°C (MPa). After 24h Curing at RT. PVC 7 +/- 1. | not stated | 6–8 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 382 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 402 Lap Shear Strength ISO 4587: … PVC N/mm2 (psi) 6 | not stated | 6 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 410 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 411 Cured for 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² >6 | not stated | > 6 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 416 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4161 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 422 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4541 PVC N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 455 PVC * N/mm² 6 | not stated | 6 MPa | ISO 4587 | TDS p.p1 |
| LOCTITE 499 PVC N/mm² 6 to 20 | not stated | 6–20 MPa | ISO 4587 | TDS p.p1 |
| Born2Bond Structural Lap shear strength (ISO 4587) @ 23°C (MPa). After 24 hours curing @ RT. PVC 5 +/- 1. | not stated | 4–6 MPa | ISO 4587 | TDS p.3 |
| LOCTITE 380 After 24 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² >4 | not stated | > 4 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 404 Lap Shear Strength, ISO 4587: PVC N/mm² >4. After 24 hours @ 22 °C. | not stated | > 4 MPa | ISO 4587 | TDS p.1 |
| LOCTITE 4471 PVC N/mm² 4 to 8 | not stated | 4–8 MPa | ISO 4587 | TDS p.p2 |
| Loctite 414 Adhesive Properties. After 24 hours @ 22 °C. Lap Shear Strength: Steel (grit blasted) 18 to 26 N/mm²; Aluminum (etched) 11 to 19 N/mm²; ABS >6; PVC >4; Polycarbonate >5; Phenolic 5 to 15; Neoprene >10; Nitrile >10 N/mm². | not stated | > 4 MPa | ISO 4587 | TDS p.1 |
| SikaFast-2590 PVC 4 MPa S | not stated | 4 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4851 PVC N/mm² 3 to 7 | not stated | 3–7 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 4861 PVC N/mm² 3 to 6 | not stated | 3–6 MPa | ISO 4587 | TDS p.p2 |
| LOCTITE 408 Cured for 72 hours @ 22 °C Lap Shear Strength, ISO 4587: … PVC N/mm² 2.8 | not stated | 2.8 MPa | ISO 4587 | TDS p.2 |
| LOCTITE 4031 After 24 hours @22°C Lap Shear Strength, ISO 4587: … PVC N/mm2 (psi) 2 to 8 | not stated | 2–8 MPa | ISO 4587 | TDS p.2 |