12 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| 3M Scotch-Weld Urethane Adhesive DP640 Overlap Shear Strength. 7 d at 23°C. ABS IPA Wipe/Abrade/IPA Wipe 1,729 lb/in² | abraded | 11.92 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| LOCTITE UK M-06FL Block Shear Strength, ASTM D 4501: ABS N/mm² 6.4 (psi) (930) | not stated | 6.4 MPa | ASTM D 4501 | TDS p.2 |
| 3M Scotch-Weld Multi-Material Composite Urethane Adhesive DP6330NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS MEK/Abrade/MEK 4.5 MPa (650 lb/in²) (AF ) ¹ | abraded | 4.5 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP604NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS IPA Wipe/Abrade/IPA Wipe 4.41 MPa (640 lb/in²) ¹ | abraded | 4.41 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP605NS ABS IPA/abrade/IPA 640 | abraded | 4.41 MPa | ASTM D1002 | TDS p.p3 |
| 3M Scotch-Weld Urethane Adhesive DP620NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS IPA Wipe/Abrade/IPA Wipe 4.34 MPa (630 lb/in²) ¹ | abraded | 4.34 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2040 A/B Average lap shear strength, plastic-plastic joints, lightly abrade and alcohol degrease pre-treatment, psi. ISO 4587. ABS 609 psi | abraded | 4.2 MPa | ISO 4587 | TDS p.3 |
| Dev-Thane 2 Cured 7 Days @ 75°F (24°C). Adhesive Tensile Lap Shear [ABS] 630 psi, 4 MPa (Subst. Fail.) Adhesive Tensile Shear ASTM D 1002 | not stated | 4 MPa | ASTM D1002 | TDS p.1 |
| 3M Scotch-Weld Urethane Adhesive DP600 Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS IPA Wipe/Abrade/IPA Wipe 500 lb/in² ¹ | abraded | 3.45 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP600NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … ABS IPA Wipe/Abrade/IPA Wipe 500 lb/in² ¹ | abraded | 3.45 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2015-1 A/B Plastic to plastic joints. Panels lightly abraded and degreased with IPA, cured 7 days at 25°C. ABS 240 psi ASTM D-1002 | abraded | 1.65 MPa | ASTM D1002 | TDS p.2 |
| 3M Scotch-Weld Multi-Material Composite Urethane Adhesive DP6310NS Overlap Shear Strength. 7 d at 23°C. ABS MEK/Abrade/MEK 1.6 MPa (230 lb/in²) | abraded | 1.6 MPa | ASTM D1002, ISO 4587 | TDS p.2 |