Polyurethane adhesive on PVC
9 verified lap-shear rows from manufacturer datasheets. Values stay with the surface preparation printed on the sheet.
| Product | Prep | Strength | Standard | Source |
|---|---|---|---|---|
| LOCTITE UK M-06FL Block Shear Strength, ASTM D 4501: PVC N/mm² 8.5 (psi) (1,230) | not stated | 8.5 MPa | ASTM D 4501 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP640 Overlap Shear Strength. 7 d at 23°C. Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 1,180 lb/in² | abraded | 8.14 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP604NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 4.27 MPa (620 lb/in²) ¹ | abraded | 4.27 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP605NS Rigid PVC IPA/abrade/IPA 620 | abraded | 4.27 MPa | ASTM D1002 | TDS p.p3 |
| ARALDITE 2040 A/B Average lap shear strength, plastic-plastic joints, lightly abrade and alcohol degrease pre-treatment, psi. ISO 4587. PVC 551 psi | abraded | 3.8 MPa | ISO 4587 | TDS p.3 |
| 3M Scotch-Weld Urethane Adhesive DP620NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 3.3 MPa (480 lb/in²) ¹ | abraded | 3.3 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP600NS Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 450 lb/in² ¹ | abraded | 3.1 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| 3M Scotch-Weld Urethane Adhesive DP600 Overlap Shear Strength … Dwell Time: 7 d … Test Method: ASTM D1002, ISO 4587 … Polyvinyl chloride (PVC) IPA Wipe/Abrade/IPA Wipe 430 lb/in² ¹ | abraded | 2.96 MPa | ASTM D1002, ISO 4587 | TDS p.2 |
| ARALDITE 2015-1 A/B Plastic to plastic joints, lightly abraded and degreased with IPA, cured 7 days at 25°C. PVC 370 psi ASTM D-1002 | abraded | 2.55 MPa | ASTM D1002 | TDS p.2 |